本体法 ABS, POLYLAC PA-1730
特性(Properties) |
测试方法(Test Method) |
测试条件(Test Condition) |
单位(Unit) |
|
引张强度Tensile Strength |
ISO 527 |
50 mm/min |
MPa |
46 |
延伸率Tensile Elongation |
|
50 mm/min |
|
|
弯曲强度Flexural Strength |
|
2mm/min |
|
|
弯曲弹性率Flexural Modulus |
|
2 mm/min |
|
|
IZOD 冲击强度 Izod Impact Strength |
|
4mm/23 |
|
|
Charpy冲击强度 Notched Impact Strength |
|
4mm/23 |
|
|
流动系数Melt Volume Flow Rate |
ISO 1133 |
200,5kg |
cm3/10min |
|
220,10kg |
|
|||
硬度Hardness |
ASTM D785 |
- |
- |
R-116 |
密度Density |
|
23 |
|
|
软化点Vicat Softening Temp. |
ISO 306 |
10N50/hr |
|
105 |
热变形温度Heat Distortion Temp. |
ISO 75-2 |
1.8MPa annealed |
|
100 |
1.8MPa unannealed |
85 |
|||
燃烧率Flammability |
|
- |
- |
1.5mm HB |